1. The heat treatment quality of the aluminum extrusion die directly affects the service life of the extrusion die. The die is hardened by "+" tempering several times to reach the hardness requirements. Quenching is to improve the hardness of the die, and multiple tempering is to improve the toughness of the die and stabilize the internal organization. The hardness value of the die heat treatment is specified as follows: large aluminum extrusion die (F>500mm), HRC45-48; Acuan sederhana (F300~500mm), HRC47-50; Die penyemperitan kecil (F<300mm), hrc48-51;="" test="" three="" points="" on="" the="" same="" plane="" of="" a="" set="" of="" molds,="" and="" the="" hardness="" values="" of="" each="" point="" should="" be="" qualified="" within="" the="" specified="">
2. Perhatian khusus harus diberikan kepada perkara-perkara berikut dalam proses rawatan haba acuan penyemperitan:
a. Kadar pemanasan bahagian suhu tinggi harus pantas, dan masa penahanan tidak boleh terlalu lama, untuk mengelakkan pembakaran terlampau atau terlalu panas acuan penyemperitan. -- butir kasar yang terlalu panas, unsur takat lebur rendah -- terbakar terlampau dan kemasukan akan larut;
b. Marah penyemperitan aluminium mati dalam masa selepas pelindapkejutan untuk mengelakkan keretakan;
c. Apabila kekerasan die penyemperitan didapati tidak mencukupi atau tidak sekata selepas rawatan haba, ia perlu disepuhlindapkan, dan rawatan haba perlu dijalankan semula mengikut proses (apabila nilai kekerasan kurang daripada HRC35, penyepuhlindapan tidak dibenarkan, dan rawatan haba dijalankan secara langsung);
d. Untuk die penyemperitan aluminium yang besar atau die siap dengan rongga kompleks, pengurangan tegasan dan proses pembajaan perlu ditambah (untuk menghapuskan tekanan pemesinan dan pemesinan elektrik, iaitu, untuk menghapuskan tekanan terma dan tekanan organisasi);
e. Sekiranya suhu minyak pelindapkejutan mati? 100 darjah untuk memastikan kesan pelindapkejutan.